分类温度：
    l普通型硅酸纤维棉 1100℃
    l标准型硅酸纤维棉 1260℃
    l高纯型硅酸纤维棉 1260℃
    l高纯型硅酸纤维棉 1360℃
    l锆铝型硅酸纤维棉 1360℃
    l含锆型硅酸纤维棉 1430℃
    Classfication Temperature:
    l COM Swinging Fibre 1100℃
    l ST Swinging Fibre1260℃
    l HP Swinging Fibre 1260℃
    l HA Swinging Fibre 1360℃
    l HAZ Swinging Fibre 1360℃
    l HZ Swinging Fibre 1430℃
    生产工艺及产品特点：
    l普通型硅酸铝纤维棉，以硬质粘土熟料为原料，经电阻炉熔融，喷吹或甩丝成纤工艺生产而成。
    l高纯型、高铝型硅酸铝纤维棉，经高纯氧化铝硅石粉合成料为原料。经电阻炉熔融，喷吹或甩丝成纤工艺生产而成。
    l含锆型硅酸铝纤维棉，以高纯氧化铝硅石粉及锆英纱合成为原料，经电阻炉熔融，喷吹或甩丝成纤工艺生产而成。
    Producing Technology
    l Com Swinging Fibre ,adopting Flint Clay as the material, melted by Resistance Furnace,is prlduced by swinging technology.
    l HP, HA Swinging Fibre, adopting HP Alumina, Silica Powder as the material,material by Resistance Furnace, is prlduced by swinging technology.
    l HZ Swinging Fibre, adopting HP Alumina, Silica Powder,Zirconia, as the material, melted by Resisance Furance, blowing or swinging, is produced by seinging technology.
    甩丝纤维棉特点：
    l甩丝纤维长，渣球含量低、低非纤维物质含量，未经处理的甩丝成纤工艺生产的长纤维，是高温窑炉加热装置壁衬缝隙填充材料，而且优良的可纺性是纺织品的原料。
    Characteristics of Swinging File:
    l Containing lube, low ball sediment, low nonfibre. Longswinging fibre without being processed is the material filled of high-temperature furnace hest-adding equipment.
    喷吹纤维棉的特点：
    l不含润滑剂，未经处理，低渣球含量，喷吹成纤工艺生产的纤维是高温窑炉的填充材料和真空成型制品，纤维喷涂，纤维纸的优良原料。
    Chaacteristics of Blowing Fibre:
    l No lube, no processed, low ball sediment. Blown fibre is the material filled of high temperature furnace.Vacuum moulding ware. Fibre spraying and xmearing ware and fibre paper.
    技术特性：
    l低导热率、低热容量
    l不含腐蚀性物质
    l优良的隔热、吸音性
    Characteristics:
    l Low thermal conductivity and heat
    l No corrosive agent
    l Excellent heat insulation and sound absorption
    应 用：
    l纤维纸及真空成型制原料
    l纤维喷涂料原料
    l纤维浇注料、涂抹料原料
    l高温窑炉加热装置壁衬缝隙填充材料
    l纤维纺织制品原料
    Usage:
    l Material of Fiber paper and vacuum moulding ware
    l Material of fiber pouring and daubing materisl
    l Materisl of Fiber pourin and daubing material
    l Material filled high-temperature furnace heat-adding equipment
    l Materisl of fiber textile
    项目 品名普通型标准型高纯型高铝型锆铝型含锆型
    分类温度 ℃110012601260136013601430
    工作温度 ℃＜100010501100120012001350
    颜 色白洁白洁白洁白洁白洁白
    体积密度Kg/m3961289612896128961609616096160
    永久线收缩（％）（保温24小时，体积密度128 Kg/m3）-4（1000℃）-3（1000℃）-3（1000℃）-3（1000℃）-3（1000℃）-3（1000℃）
    各热面温度下导热系数 （w/n.k）体积密度Kg/m30.09（400℃）
    0.176（800℃）0.09（400℃）
    0.176（800℃）0.09（400℃）0.176（800℃）0.22（1000℃）0.132（600℃）
    0.22（1000℃）0.132（600℃）
    0.22（1000℃）0.76（600℃）
    0.22（1000℃）
    抗拉强度 Mpa(体积密度128Kg/m3)0.08-0.120.08-0.120.08-0.120.08-0.120.08-0.120.08-0.12
    化
    学
    组
    成
    ％AL2O342-4445-4647-4952-5545-4639-40
    AL2O3+SIO296979999－－
    AL2O3+SIO2+ZrO2－－－－9999
    ZrO2－－－－5-715-17
    Fe2O3＜1.2＜1.00.20.20.20.2
    Na2O+K2O≤0.5≤0.50.20.20.20.2
    产品尺寸（mm）常用规格7200×610×10－50；其它规格根据用户要求制作